Abstract
The excellent mechanical properties of Inconel 718 are due to the γ′ and specifically the γ″ precipitates. Solution heat treatment was performed at 1095 °C for 1 h followed by air cooling. A δ-phase precipitation heat treatment was made at 955 °C, 1 h/AC. Finally a double-aging at 720 °C, 8 h/FC at 57 °C/h down to 620 °C, 8 h/AC to precipitate both γ′ and γ″ phases. The precipitation of both γ′ and γ″ phases were studied in details after aging treatment by the use of transmission electron microscopy. The spherical precipitates were identified as γ′ phase and the ellipsoidal precipitates were γ″ phase. At 720 °C for 8 h both γ′ and γ″ are growing; the mean long-axis of γ″ particle is 40 nm and the mean short-axis is 14 nm whereas the average diameter of the spherical γ′ particle is 17 nm. However, at 620 °C, γ″ stops growing but γ′ continue to grow and the diameter increases to 21 nm.