Abstract
We studied the structure and magnetic properties of molecular-beam epitaxygrown 300 Å thick Fe/Pt multilayers with different bilayer thickness andannealing temperature. The Fe/Pt multilayers were deposited on 100 Å thick Ptbuffer layers at 100 °C100 °C on Al2O3Al2O3 (0001) substrates. The structure of as-deposited Fe/Pt films was fcc(111). While the postannealing temperature ⩾400 °C,⩾400 °C, an additional FePt(100) orientation was observed. A large coercivity range, namely, 200–16 000 Oe can be tuned by varying the bilayer thickness andannealing temperature.