Abstract
This study examines the post-annealing-dependent behaviors of the shallow junction produced by implanting 10 15 cm -2 20 keV BGe ions into n-type 〈100〉 silicon specimens. Post-annealing treatments consisted of one- and two-step annealing including both furnace annealing (FA) and rapid thermal annealing (RTA). Comparison of the one-step FA at 550°C and the one-step RTA at 1050 °C revealed that boron depth profiles were slightly diffused in the former but exhibited considerable transient-enhanced diffusion (TED) in the latter. However, both the one-step FA- and RTA-annealed germanium depth profiles barely diffused, while the latter diffusing slightly deeper than the former. The optimum value of junction depth (x j ) times sheet resistance (R s ) was obtained with one-step FA at 550 °C for 1 h. The two-step annealing (FA at 550 °C and RTA at 1050 °C) results showed that the RTA-induced TED in the boron depth profiles could be effectively retarded only when FA took place for more than 3 h. Again, germanium depth profiles are also barely diffused while the corresponding TEDs were larger than those in one-step FA but smaller than those in one-step RTA. Furthermore, the two-step annealing of FA at 550 °C for 3 h followed by RTA at 1050 °C for 30 s is suggested when attempting to obtain an optimum value of x j R s . © 2005 Elsevier B.V. All rights reserved.