摘要
First-principles calculation has become one of the most reliable approaches in predicting structural, electronic, and magnetic properties for material applications. Alloys in Heusler structures have also attracted much attention recently since they can be easily synthesized and provide interesting properties for future spintronic applications. In this work, we investigate a series of Fe-based Heusler compounds Fe 3−x Y x Z (x = 0, 1, 2, 3; Y= Cr, Mn, Co; Z= Al, Ga, Si) with L2 1 - and XA-type structures using first-principles calculations based on density functional theory. According to formation energy calculations and mechanical property analysis, most of the studied Heusler compounds are thermodynamically stable and could be synthesized experimentally. The Co substitution leads Fe 3−x Co x Z to a ferromagnetic ground state like Fe 3 Z with a strong magnetization ranging from 4 to 6 μ B /f. u. While replacing Fe with Cr or Mn, the exchange coupling between Cr (Mn) and its neighboring atoms generally tend to be anti-parallel. Among the antiferromagnetic compounds, Mn 3 Al and Mn 3 Ga are antiferromagnetic half metal while Mn 3 Si is ferrimagnetic half metal. These rarely found type of half metals with low magnetic moment and high spin polarization at the Fermi level are important for low energy consumption spintronic applications. The estimated Curie temperatures for Mn 3 Al, and Mn 3 Si and Co2FeSi (XA) are in good agreement with previously theoretical values, while for Fe 3 Al and Fe 3 Si, they are in good agreement with previous experimental results. The good consistency in Curie temperature demonstrates high reliability of our predictions based on first-principles calculations. As for the topological property aspect, we predict Fe 2 CrAl and Fe 2 MnAl as the 3-dimensional Weyl semimetal. Furthermore, Fe 2 CrSi is predicted to be the magnetic nodal-line semimetal. Interestingly, our mechanical property analysis demonstrates that Co 3 Si and Fe 2 CoSi (L2 1 ) exhibit ultraelastic metal behavior, which is of high potential in advanced mechanical industry. This work suggests that Heusler compounds are excellent candidates for future spintronics as well as for high-performance ultraelastic metals.