摘要
Purpose: Surface characteristics of orthodontic miniscrews might affect survival rates and removal torque values (RTVs). This experimental study aimed to clarify whether and why a microporous or nanoporous surface promotes higher survival rates and RTVs for orthodontic miniscrews. Methods: Using a split-leg design, one set each of nonporous (sham control, n = 24) and microporous (control, n = 6), and three sets of nanoporous (experimental, n = 6 per set) miniscrews were implanted in the tibias of 12 New Zealand rabbits and immediately loaded with 1.5 N nickel–titanium coil springs for 12 weeks. The surface morphology, micropores, and nanotube diameters of the miniscrews were examined using scanning electron microscopy and field-emission scanning electron microscopy. The surface composition and thickness were determined using Auger electron spectroscopy. The survival rates and RTVs of each set were assessed. Results: The nanoporous miniscrews had higher survival rates, RTVs (p < 0.001), and thicker nanotube oxide thicknesses (p < 0.001) than the nonporous and microporous miniscrews. The nonporous and microporous miniscrews had no nanotube structures. The surface oxide composition was titanium dioxide (TiO 2 ). The threshold RTV, TiO 2 thickness, and nanotube diameter of nanoporous miniscrews needed to promote the experimental survival rate to 100% was determined to be 6.6 ± 0.8 N-cm (p < 0.05), 22.5 ± 4.8 nm (p < 0.05), and 17.6 ± 2.3 nm or above, respectively. Conclusion: Nanoporous surfaces promoted higher survival rates and RTVs than microporous miniscrews. This could be due to TiO 2 nanotube structures with thicker oxide layers in nanoporous miniscrews.