Abstract
The kinetics of hydrogen-induced slow crack growth (SCG) under constant load was studied in two stainless steel alloys containing mixtures of bcc and fcc phases. FERRALIUM 255, a duplex stainless steel, consisting of ∼50 pct austenite in a ferrite matrix, was tested in hydrogen gas at 0 to 100 °C with the loading axis both perpendicular and parallel to the rolling direction. In addition, specimens of AISI 301 were deformed in air in different ways to produce various amounts of bcc phase in an austenite matrix prior to testing in H 2 gas at room temperature. The kinetics of subcritical slow crack growth (SCG) in these alloys was compared with that for austenitic and for ferritic stainless steels. The SCG rates were rationalized in terms of differences in hydrogen permeation in the two phases. The results confirm that a higher rate of supply and accumulation of hydrogen in the region ahead of the crack tip allows a higher cracking velocity. © 1988 The Metallurgical Society of AIME.