摘要
Direct deposition of high-quality Ge film on Si substrate suitable for fabricating Ge/Si photodiodes was achieved by using plasma-enhanced chemical vapor deposition (PECVD) with GeCl <sub>4</sub> /H <sub>2</sub> as precursors. A tensile-strained, impurity-free, monocrystalline Ge film with a surface roughness of < 1 nm and a threading-dislocation density on the order of 10 <sup>4</sup> cm <sup>−2</sup> could be grown at a rate of ca. 80 nm/min at a substrate temperature of 450 °C directly without the need of any kind of buffer layer or post-annealing. When applied to fabricate near-infrared (NIR) photodiodes, a low dark current density and a reasonably good responsivity for the employed photodiode architecture were attained, revealing the potential of this low-temperature fabrication method in monolithic integration of optoelectronic components with Si-based electronic circuits. The success of this technique may be attributed to an atomic-layer-deposition-like process for both nucleation and growth.