Abstract
Fatigue behavior of carbon fiber reinforced poly etheretherketone (PEEK) laminated composite was investigated. The [±45] 4s AS-4/PEEK laminated composites under static tensile measurement at various test temperatures were conducted. Three tension-tension fatigue loading frequencies, 1 Hz, 5 Hz and 10 Hz, were selected to study the effect of frequency on the fatigue behavior of [±45] 4s AS-4/PEEK laminate. The survival probability of experimental fatigue life data under different stress amplitude tests were estimated and analyzed by the median rank order-statistic cumulative-distribution function and the Weibull distribution function. The S-N curves at different fatigue loading frequencies exhibited a trend of two-segment straight line curves. The increase in surface temperature of specimens was found and the thermal stress history was also investigated by thermo-image techniques during fatigue life testing. The fatigue failure mechanism was investigated by X-ray radiography. © 1995 Polymer Society.