Abstract
The effects of 2.245 GeV Au-ion irradiation and subsequent annealing processes on the evolution of microstructure of diamond films with microcrystalline (MCD) or ultra-nanocrystalline (UNCD) granular structure were investigated, using near edge x-ray absorption fine structure and electron energy loss spectroscopy in transmission electron microscopy. For MCD films, the Au-ion irradiation disintegrated some of the diamond grains, resulting in the formation of nano-sized carbon clusters embedded in a matrix of amorphous carbon (a-C). The annealing process recrystallized the diamond grains and converted the a-C into nano-sized graphite particulates and, at the same time, induced the formation of nano-sized i-carbon clusters, the bcc structured carbon with a 0 0.432 nm. In contrast, for UNCD films, the Au-ion irradiation transformed the grain boundary phase into nano-sized graphite, but insignificantly altered the crystallinity of the grains of the UNCD films. The annealing process recrystallized the materials. In some of the regions, the residual a-C phases were transformed into nano-sized graphites, whereas in other regions i-carbon nanoclusters were formed. The difference in irradiation-induced microstructural transformation behavior between the MCD and the UNCD films is ascribed to the different granular structures of the two types of films. © 2013 American Institute of Physics.