Abstract
Single crystal ferromagnetic Fe3Si(111) films were grown epitaxially on GaAs(111)A by molecular beam epitaxy. These hetero-structures possess extremely low surface roughness of 1.3 and interfacial roughness of 1.9, measured by in-situ scanning tunneling microscope and X-ray reflectivity analyses, respectively, showing superior film quality, comparing to those attained on GaAs(001) in previous publications. The atomically smooth interface was revealed by the atomic-resolution Z (atomic number)-contrast scanning transmission electron microscopy (STEM) images using the correction of spherical aberration (Cs)-corrected electron probe. Excellent crystallinity and perfect lattice match were both confirmed by high resolution x-ray diffraction. Measurements of magnetic property for the Fe3Si/GaAs(111) yielded a saturation moment of 990 emu/cm3 with a small coercive field ≤1 Oe at room temperature.