Abstract
The high-frequency characteristics of the RF integrated inductors with antiferromagnetic/ferromagnetic (AF/F) multilayers (MLs) are studied. Each AF layer is 8-nm IrMn and F is Co 50 Fe 50 with a 200-nm splitting into N = 1 to 5 repeats of MLs. This exchange coupled {IrMn/CoFe(d nm)} N MLs are deposited on top of the two-port inductors with five-turn square spiral coils, a dimension of 100 μm × 100 μm and line/space of 5μm/2 μm. The inductor surface and magnetic layer is separated by 1-μm-thick SiO 2 . The enhancement of inductance (ΔL) is 20% compared to an air-core of the same coil size. The resonance peak gradually shifted to a higher frequency with increasing N, and reached at a maximum of 4.3 GHz when N = 5. This is in good agreement with our magnetic data which revealed that the anisotropy field (H k ) and ferromagnetic resonance frequency (f FMR ) of {IrMn/CoFe(d nm)} N MLs are increased with increasing N. The quality factor, Q is improved by 6.8% at 1.5 GHz for the {IrMn/CoFe(40 nm)} N=5 integrated inductors compared to air-core inductors. © 2007 IEEE.