摘要
This study examines the facet-dependent optical properties of size-tunable Ag-Cu 2 O core-shell nanocrystals with 38, 42, and 50 nm cubic Ag cores. The Ag cores were prepared from octahedral Au seeds. The Cu 2 O shells are single-crystalline. In the case of Au@Ag-Cu 2 O nanocrystals with 42 nm Ag cores, the Ag surface plasmon resonance (SPR) absorption band at 485 nm has been widely red-shifted to 730, 755, and 775 nm for rhombic dodecahedra, truncated octahedra, and cuboctahedra, respectively, after forming the Cu 2 O shells. The Ag SPR band positions are mostly fixed despite large changes in the shell thickness, showing the presence of facet-dependent optical properties. Because of the strong Ag SPR band absorption, all samples exhibit a better photothermal activity than that of Au-Cu 2 O nanocrystals. Facet-dependent heat transmission may be present for particles with a Ag SPR band much deviated from the laser wavelength, but this phenomenon is lost for particles with an SPR band approaching the excitation wavelength as the particles become highly photothermally efficient to give solution temperatures of 80-95 °C within 3 min of laser irradiation.