摘要
A bimorph composed of ferrimagnetic cobalt ferrite (CoFe 2 O 4 , CFO) and flexible muscovite was fabricated via van der Waals epitaxy. The combination of X-ray diffraction and transmission electron microscopy was conducted to reveal the heteroepitaxy of the CFO/muscovite system. The robust magnetic behaviors against mechanical bending were characterized by hysteresis measurements and magnetic force microscopy, which maintain a saturation magnetization (M s ) of ∼120-150 emu/cm 3 under different bending states. The large magnetostrictive response of the CFO film was then determined by digital holographic microscopy, where the difference of magnetostrction coefficient (δ λ) is -104 ppm. The superior performance of this bimorph is attributed to the nature of weak interaction between film and substrate. Such a flexible CFO/muscovite bimorph provides a new platform to develop next-generation flexible magnetic devices.