A microwave-assisted hydrothermal method has been developed as an efficient approach to readily induce phase transition of titanate assemblies in conjunction with decoration of Cu 2 O clusters on the surface. The influence of Cu 2+ ions on the hydrothermally induced structural evolution was examined, and the roles of heterojunctions in the resulting composites in charge separation for improved photocatalytic activity were clarified. Hierarchical titanate assemblies with high adsorption capacity for Cu 2+ ions (95.7 mg/g) were prepared from a low alkaline condition. Microwave-assisted hydrothermal treatment was then used to transform the adsorbents into Cu 2 O/titanate/titania photocatalysts in 20 min via inducing titanate-to-titania and Cu 2+ -to-Cu 2 O dual transitions. While tubular architecture was maintained in the composites, the Cu 2 O clusters highly dispersed on the surface. Adsorbed Cu 2+ ions have been found to retard the titanate-to-titania transformation locally, thus leading to Cu 2 O/titanate/titania heterojunctions. The multiheterojunctions enabled the composites to exhibit 1.7-5.1 times higher activity than the commercial product P25 (k obs , 0.06 min -1 ) for decomposition of bisphenol A due to charge separation. EPR results clearly reveal that the type II band alignment effectively drove electrons and holes to migrate toward the titania and the Cu 2 O moieties, respectively, and the titanate moiety positioning in between prevented back recombination. The optimal Cu 2 O loading to the highest activity (k obs , 0.306 min -1 ) was 3.7 wt %. Over the optimal amount, the lower reduction potential in the valence band of the Cu 2 O clusters compensated for the positive effect from charge separation, thus causing the activity to decline in turn.