摘要
The most pressing barrier for the development of advanced electronics based on two-dimensional (2D) layered semiconductors stems from the lack of site-selective synthesis of complementary n- A nd p-channels with low contact resistance. Here, we report an in-plane epitaxial route for the growth of interlaced 2D semiconductor monolayers using chemical vapor deposition with a gas-confined scheme, in which patterned graphene (Gr) serves as a guiding template for site-selective growth of Gr-WS <sub>2</sub> -Gr and Gr-WSe <sub>2</sub> -Gr heterostructures. The Gr/2D semiconductor interface exhibits a transparent contact with a nearly ideal pinning factor of 0.95 for the n-channel WS <sub>2</sub> and 0.92 for the p-channel WSe <sub>2</sub> . The effective depinning of the Fermi level gives an ultralow contact resistance of 0.75 and 1.20 kω·μm for WS <sub>2</sub> and WSe <sub>2</sub> , respectively. Integrated logic circuits including inverter, NAND gate, static random access memory, and five-stage ring oscillator are constructed using the complementary Gr-WS <sub>2</sub> -Gr-WSe <sub>2</sub> -Gr heterojunctions as a fundamental building block, featuring the prominent performance metrics of high operation frequency (>0.2 GHz), low-power consumption, large noise margins, and high operational stability. The technology presented here provides a speculative look at the electronic circuitry built on atomic-scale semiconductors in the near future.