Abstract
The unique morphology of Ti O2 nanorods grown in a two-step thermal evaporation process under a controlled atmosphere was observed. The first step attempts to form Ti O2 seeds with a higher surface energy on the alumina substrate with lower surface energy; the second step is the growth of the Ti O2 seeds gradually to form nanorods. Field emission scanning electron microscopy and Raman spectrometry were used to elucidate the morphology and the characteristic spectra, respectively. The nanorods were composed of nanobricks. The nanorods were 70-150 nm in diameter and up to 2 μm long, respectively. High-resolution transmission electron microscopy demonstrated that an individual nanorod exhibits a twin structure with a body-centered tetragonal rutile phase, and grows in the [110] direction. Its optical response shows a broad blue emission peak at ∼418 nm as cathodoluminescence analysis. © 2005 American Vacuum Society.