Abstract
The isothermal oxidation resistance of Al 0.2 Co 1.5 CrFeNi 1.5 Ti 0.3 high-entropy alloy is analyzed and the microstructural evolution of the oxide layer is studied. The limited aluminum, about 3.6 at %, leads to the non-continuous alumina. The present alloy is insufficient for severe circumstances only due to chromium oxide that is 10 μm after 1173 K for 360 h. Thus, the aluminized high-entropy alloys (HEAs) are further prepared by the industrial packing cementation process at 1273 K and 1323 K. The aluminizing coating is 50 μm at 1273 K after 5 h. The coating growth is controlled by the diffusion of aluminum. The interdiffusion zone reveals two regions that are the Ti-, Co-, Ni-rich area and the Fe-, Cr-rich area. The oxidation resistance of aluminizing HEA improves outstandingly, and sustains at 1173 K and 1273 K for 441 h without any spallation. The alumina at the surface and the stable interface contribute to the performance of this Al 0.2 Co 1.5 CrFeNi 1.5 Ti 0.3 alloy.