摘要
We report on the first demonstration of metal-insulator-semiconductor-type plasmonic lasers at the telecom wavelength (∼1.3 μm) using top-down fabricated semiconductor waveguides on single-crystalline metallic platforms formed using epitaxially grown Ag films. The critical role of the Ag film thickness in sustaining plasmonic lasing at the telecom wavelength is investigated systematically. Low-threshold (0.2 MW/cm 2 ) and continuous-wave operation of plasmonic lasing at cryogenic temperatures can be achieved on a 150 nm Ag platform with minimum radiation leakage into the substrate. Plasmonic lasing occurs preferentially through higher-order surface-plasmon-polariton modes, which exhibit a higher mode confinement factor, lower propagation loss, and better field-gain coupling. We observed plasmonic lasing up to ∼200 K under pulsed excitations. The plasmonic lasers on large-area epitaxial Ag films open up a scalable platform for on-chip integrations of plasmonics and optoelectronics at the telecom wavelength.