摘要
A series of cubic network phases was obtained from the selfassembly of a single-composition lamellae (L)-forming block copolymer (BCP) polystyrene-block-polydimethylsiloxane (PS-b-PDMS) through solution casting using a PS-selective solvent. An unusual network phase in diblock copolymers, double-primitive phase (DP) with space group of Im3m, can be observed. With the reduction of solvent evaporation rate for solution casting, a double-diamond phase (DD) with space group of Pn3m can be formed. By taking advantage of thermal annealing, order-order transitions from the DP and DD phases to a double-gyroid phase (DG) with space group of Ia3d can be identified. The order-order transitions from DP (hexapod network) to DD (tetrapod network), and finally to DG (trigonal planar network) are attributed to the reduction of the degree of packing frustration within the junction (node), different from the predicted Bonnet transformation from DD to DG, and finally to DP based on enthalpic consideration only. This discovery suggests a new methodology to acquire various network phases from a simple diblock system by kinetically controlling selfassembling process.