Abstract
The hydrogen absorption characteristics of TiFe partially substituted with a small amount of chromium or manganese for iron were studied. The morphology of the specimen surface was examined and the phases in the sample were identified. The microscopic composition differences for the individual phases were analysed. It was observed that the samples required no activation for hydrogenation when a second phase was present. Increasing the amount of second phase led to a higher activation rate, lower plateau pressure and higher maximum absorption capacity. Homogenization treatment at 900 °C reduced the activation rate but had no effect on the subsequent hydrogenation properties. The effects of substitution and homogenization on the hydrogenation of TiFe were correlated with the quantity and morphology of the second phase. © 1992.