Abstract
The high-temperature corrosion behavior of cold-rolled and annealed 304 stainless steel (304SS) and Fe-29Mn-8Al-2.5Si-2Cr-0.74C alloy coated with 0.002 g cm -2 NaCl initially were studied at 900°C in air. The corrosion kinetics of the two alloys follow the parabolic rate law. The initial NaCl coating accelerates oxidation of these alloys by oxychlorination and chlorination/oxidation cyclic reactions, and catalytic actions of chloride or chlorine are thought to be the principal causes. A bulky, layered scale as well as some intergranular attack is noted on the annealed 304SS, and intergranular attack distributes over the alloy substrate of the cold-rolled 304SS during a 144 h exposure. With the formation of a compact Al 2 O 3 scale to decrease further chlorine attack, the corrosion resistance of Fe-Mn-Al alloy, is superior to that of 304SS in this study. © 2003 Kluwer Academic Publishers.