摘要
Abstract: A new strategy was demonstrated to produce cellulose nanofibril-silica (CNF–SiO 2 ) nanocomposite membrane separator for supercapacitor by one-pot synthesis of silica (SiO 2 ) nanoparticles using different contents of tetraethyl orthosilicate (TEOS) precursor (0.9, 1.8, 2.7, 3.6 wt%). With the SiO 2 nanoparticles acting as the disassembling agent, a highly porous CNF–SiO 2 nanocomposite membrane was prepared using a simple solvent casting method. The CNF–SiO 2 nanocomposite membrane with 1.8 wt% TEOS content (CNF-C2), exhibited the best properties with high porosity of 61%, electrolyte uptake ability of 260% and ionic conductivity of 5.0 mS cm − 1 . Besides, the maximum thermal degradation temperature (T max ) of the CNF–SiO 2 nanocomposite membrane increased from 300 ℃ to 322 ℃, making it suitable for use within the operating temperatures of a supercapacitor. A symmetric supercapacitor assembled with CNF-C2 separator achieved the highest specific capacitance of 179.0 F g − 1 at 0.1 A g − 1 and energy density of 35.8 Wh kg − 1 at a power density of 240.0 W kg − 1 . This CNF–SiO 2 nanocomposite membrane helped the supercapacitor to achieve excellent electrochemical stability after 10,000 charge-discharge cycles with a capacitance retention and coulombic efficiency of 98.3% and 95.0%, respectively. The presented results proved that the CNF–SiO 2 nanocomposite membrane is a good alternative separator in the supercapacitor application. Graphical abstract: [Figure not available: see fulltext.]