Abstract
Non-epitaxially induced perpendicular magnetic anisotropy (PMA) of Co 50 Pt 50 thin films at room temperature (RT) is reported. The CoPt film having a disordered hcp structure shows a magnetocrystalline anisotropy (K u RT ) of 1-2 × 10 6 erg/cm 3 in a wide range of layer thickness from 2 to 20 nm. K u RT of about 1 × 10 6 erg/cm 3 can be preserved after a 400 °C-thermal cycle in the 5-nm-thick sample. Moderate PMA, large thickness range, simple preparation process, low formation temperature but good thermal stability make presented hcp CoPt become a remarkable option for advanced spintronic devices.