摘要
Hierarchical microstructural design of high-entropy superalloys offers novel strengthening pathways beyond classical superalloys. Here we assess the strength of isolated γ’ precipitates with and without an additional internal γ nanophase. The results show that nano-precipitation within the γ’ phase leads to a marked statistical reduction of the dislocation-nucleation limited yield strength. In concert with disorder-driven chemical weakening of the γ’ phase, these findings indicate that bulk strengthening due to hierarchical microstructural design in high-entropy superalloys must primarily be pinning dominated.