摘要
The effects of Li 2 O-ZnO-B 2 O 3 addition on densification, microstructure and dielectric properties of X7R dielectric fired at 950 °C in a reducing atmosphere have been investigated. Combined with a mixture of Li 2 CO 3 , H 3 BO 3 and ZnO (LZB-M), the resulting low-fire dielectric composites are more densified with a higher dielectric constant than those prepared by using a Li 2 O-ZnO-B 2 O 3 glass (LZB-G). This is attributed to the high densification, large grain size and formation of a core-shell structure observed in the X7R+LZB-M dielectric composite