Abstract
A stable magnetically recyclable extraordinary photocatalyst for Fenton-like processes, Pt coupled ZnFe 2 O 4 nanocrystals (Pt/ZnFe 2 O 4 ), was developed, which makes possible the shortening of photodegradation treatment times from hours to seconds. Pt/ZnFe 2 O 4 nanocrystals (NCs) were prepared by simply mixing ZnFe 2 O 4 NCs with Pt NCs, produced by a carrier solvent assisted interfacial reaction process and a polyol process, respectively. The extraordinary organic pollutant degradation efficiency of the Pt/ZnFe 2 O 4 NCs was demonstrated with rhodamine B (RhB) degradation in a Fenton-like process under illumination of simulated sunlight at 100 mW cm -2 . The apparent reaction rate constant can reach as high as 9.31 min -1 , almost three orders of magnitude higher than 0.01 min -1 typically achieved by photocatalysts reported in the literature. The excellent magnetic recyclability and cycling stability of the Pt/ZnFe 2 O 4 NCs toward RhB degradation were also demonstrated. A degradation mechanism was proposed to show how the coupling of Pt enhances the charge separation of ZnFe 2 O 4 NCs and generation of HO 2 . and HO . , all significant factors to boost the RhB degradation efficiency. The Pt/ZnFe 2 O 4 NCs prove to be an extremely efficient and promising catalyst for Fenton-like processes for the removal of recalcitrant organic pollutants and greatly increase the competitiveness and practicality of photocatalytic degradation in pollutant control.