摘要
This study reports a self-induced ferroelectric Ge-doped HfO2 (Ge:HfO2) thin film through interface reactions. In the first experiment, three treatments for forming interfacial layer (IL) were discussed through TiN/2-nm-thick Al2O3/2-nm-thick Ge:HfO2/GeO2/Ge metal-ferroelectric-insulator-semiconductor capacitors. The remnant polarization (P-r), leakage current, and interface trap density (D-it) were compared to select the most appropriate IL treatment. The results show that the in-situ ozone treatment under the standard atomic layer deposition process had the second highest 2P(r) value as well as lower D-it values. Next, the thicknesses of Al2O3/Ge:HfO2 would be changed to 4 nm/2 nm and 3 nm/3 nm to investigate the ferroelectricity and leakage current. Although the 3-nm-thick Al2O3/3-nm-thick Ge:HfO2 shows a lower 2P(r) value, the leakage current is much lower than 2-nm-thick Al2O3/2-nm-thick Ge:HfO2. The self-induced ferroelectric 3-nm-thick Ge:HfO2 thin film was then applied to fabricate Ge stacked nanowires gate-all-around field-effect transistor. The results show a steep subthreshold slope of 58 mV/dec for pFET and on-off current ratio > 10(5) and have high potential in low-power IC applications.