Abstract
Amorphous coatings, particular nitride systems, are of interest for numerous practical applications. Nevertheless, at present only a few amorphous nitride coating systems have been considered, the most notably being the (TM, Si)N system (transition metal (TM) = Ti, Zr, W, Mo). The present study provides an alternative approach for producing amorphous nitride films with high thermal stability up to 700 °C for 2 h. Films are deposited from an equimolar AlBCrSiTi target in various argon/nitrogen atmospheres at different substrate temperatures. It is found that above the nitrogen flow ratio (i.e. R N = N 2 /N 2 + Ar) of 28.6% a near equal ratio between target elements and nitrogen is approached, thus indicating the coatings have the chemical formula of (AlBCrSiTi)N. The glancing-angle X-ray diffractometer and transmission electron microscope investigations indicate that the coatings, regardless of nitrogen concentration or deposition temperature (up to 500 °C), are amorphous. Thermal treatment shows that the amorphous structure of this (AlBCrSiTi)N coating is maintained up to 700 °C when annealing for 2 h in vacuum. At annealing temperatures of 800 °C and above, the amorphous films transform into a simple NaCl-type face-centered cubic solid solution. Even after annealing at 1000 °C for 2 h, the grain size is only 2 nm. High entropy effect, large lattice distortion effect, and sluggish diffusion effect are proposed to account for the formation of amorphous nitrides. © 2011 Published by Elsevier B.V. All rights reserved.