The intrinsically high cost of iridium and the poor stability of iridium-based catalysts under low-loading conditions in proton exchange membrane water electrolysis (PEMWE) remain major obstacles to large-scale deployment. A solution-phase loading method is developed to enable uniform anchoring and activation of iridium oxide (IrOx) nanoparticles on tungsten oxide nanowire (WOxNW). The resulting IrOx/WOxNW heterostructure exhibits enhanced oxygen evolution reaction (OER) activity and stability under acidic conditions. In-situ near-ambient-pressure X-ray photoelectron spectroscopy reveals effective suppression of Ir over-oxidation to high-valent species (>4+), a degradation pathway evident in Ir Black. Non-destructive XPS depth profiling shows that WOx helps stabilize a core–shell structure composed of a metallic Ir0 core and an Ir4+ shell, whereas Ir Black becomes fully oxidized under similar conditions. Together with DFT calculations, this structural feature provides a theoretical basis for the improved OER kinetics. The catalyst achieves a low degradation rate of 15.7 µV h−1 over 100 h and minimal Ir leaching (0.003 ppm) during half-cell testing at 10 mA cm−2. In PEMWE operation, it delivers 1 A cm−2 at 1.61 V for over 200 h with an Ir loading of only 0.33 mgIr cm−2. This work represents one of the few in-situ studies linking catalyst–support interactions to degradation suppression, offering a promising solution toward durable, low-Ir electrolyzers for green hydrogen production.
[Display omitted]
•2–3 nm IrOx are uniformly anchored on WOx nanowires via a solution-phase method.•In-situ NAP-XPS reveals suppressed Ir over-oxidation in IrOx/WOx heterostructure.•WOx stabilizes an Ir0/Ir4+ core–shell structure and inhibits catalyst degradation.•IrOx/WOx achieves 1 A cm−2 at 1.61 V with only 0.33 mgIr cm−2 over 200 h in PEMWE.•This work demonstrates in-situ verified stability of a low-Ir catalyst–support system.