Abstract
A quantitative study of the stability of silver nanoparticles (AgNPs) conjugated with thiolated polyethylene glycol (SH-PEG) was conducted using gas-phase ion-mobility and mass analyses. The extents of aggregation and surface dissolution of AgNPs, as well as the amount of SH-PEG adsorption and desorption, were able to be characterized simultaneously for the kinetic study. The results show that the SH-PEG with a molecular mass of 6 kg/mol (SH-PEG6K) was able to adsorb to the surface of AgNP to form PEG6K-HS-AgNP conjugates, with the maximum surface adsorbate density of ∼0.10 nm -2 . The equilibrium binding constant for SH-PEG6K on AgNPs was calculated as ∼(4.4 ± 0.9) × 10 5 L/mol, suggesting a strong affinity due to thiol bonding to the AgNP surface. The formation of SH-PEG6K corona prevented PEG6K-HS-AgNP conjugates from aggregation under the acidic environment (pH 1.5), but dissolution of core AgNPs occurred following a first-order reaction. The rate constant of Ag dissolution from PEG6K-HS-AgNP was independent of the starting surface packing density of SH-PEG6K on AgNP (σ 0 ), indicating that the interactions of H + with core AgNP were not interfered by the presence of SH-PEG6K corona. The surface packing density of SH-PEG6K decreased simultaneously following a first-order reaction, and the desorption rate constant of SH-PEG6K from the conjugates was proportional to σ 0 . Our work presents the first quantitative study to illustrate the complex mechanism that involves simultaneous aggregation and dissolution of core AgNPs in combination with adsorption and desorption of SH-PEG. This work also provides a prototype method of coupled experimental scheme to quantify the change of particle mass versus the corresponding surface density of functional molecular species on nanoparticles.