Abstract
Tungsten oxide (WO 3 ) nanoparticles (WO 3 NPs) were prepared using beetroot (Beta vulgaris) extract. The synthesis was optimized by evaluating the effect of pH during the reduction of the WO 3 precursor and sintering temperature. Physicochemical characterization of the formed nanoparticles was performed using X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and UV–visible diffuse reflectance UV–visible spectroscopy. Furthermore, the prepared WO 3 NPs were employed as photocatalyst for rhodamine B removal over the photocatalytic oxidation mechanism. Synthesis optimization revealed that a single phase of WO 3 NPs obtained by reduction at pH 4 and a sintering temperature of 550 °C. XRD and XPS measurements revealed that the single-phase WO 3 NPs was obtained with a crystallite size of 26.4 nm. SEM and transmission electron microscopy (TEM) indicated polymorphic forms, predominantly as nanorods, with a mean particle size of 24 nm. The WO 3 NPs have a band gap energy of 2.9 eV, supporting their performance as a photocatalyst. Evaluation of the photocatalytic activities of WO 3 NPs represents high activity and reusability of the material. A removal efficiency of 99.67% was achieved during 30 min of treatment under UV light illumination. A study on the effect of scavengers revealed the important role of hydroxy radicals in the photocatalysis mechanism. WO 3 NPs can be recycled and reused for photocatalysis, maintaining photoactivity for five cycles.